Het OWA, het open archief van het Waterbouwkundig Laboratorium heeft tot doel alle vrij toegankelijke onderzoeksresultaten van dit instituut in digitale vorm aan te bieden. Op die manier wil het de zichtbaarheid, verspreiding en gebruik van deze onderzoeksresultaten, alsook de wetenschappelijke communicatie maximaal bevorderen.
Dit archief wordt uitgebouwd en beheerd volgens de principes van de Open Access Movement, en het daaruit ontstane Open Archives Initiative.
Basisinformatie over ‘Open Access to scholarly information'.
Chloride induced reinforcement corrosion behavior in self-healing concrete with encapsulated polyurethane
Van Belleghem, B.; Kessler, S.; Van den Heede, P.; Van Tittelboom, K.; De Belie, N. (2018). Chloride induced reinforcement corrosion behavior in self-healing concrete with encapsulated polyurethane. Cement and Concrete Research 113: 130-139. https://dx.doi.org/10.1016/j.cemconres.2018.07.009
In: Cement and Concrete Research. PERGAMON-ELSEVIER SCIENCE LTD: Oxford. ISSN 0008-8846; e-ISSN 1873-3948, meer
|  |
| Trefwoord |
|
| Author keywords |
Concrete; Durability; Chloride; Corrosion; Self-healing |
| Auteurs | | Top |
- Van Belleghem, B., meer
- Kessler, S.
- Van den Heede, P., meer
|
- Van Tittelboom, K., meer
- De Belie, N., meer
|
|
| Abstract |
Cracks in reinforced concrete structures accelerate the ingress of chlorides and therefore cause a higher risk for corrosion. In this research, autonomous healing of cracks by encapsulated polyurethane was investigated as a possible method to reduce reinforcement corrosion. Reinforced concrete beams were exposed weekly to a chloride solution and electrochemical parameters were measured to determine the influence of the self-healing mechanism on the corrosion process. The rebars were visually examined afterwards. For the cracked beams an active state of corrosion was detected within an exposure period of 10 weeks and clear pitting corrosion was observed on the rebars. Autonomous crack healing with low viscosity polyurethane could significantly reduce the corrosion in the propagation stage. For these specimens no visual damage to the rebars was detected. In conclusion, the application of self-healing concrete with a low viscosity polyurethane is able to enhance the durability of reinforced concrete structures in marine environments. |